Abstrict
A base (2) for an electric heater comprises a compressed and heat-hardened
composition. The composition comprises: 65 to 98 weight percent
fumed silica; 1 to 15 weight percent reinforcing filaments; up to
10 weight percent pyrogenic silica; and up to 20 weight percent
opacifier. A method of manufacturing the base is also disclosed.
Claims
We claim
1. A base for an electric heater comprising a compressed and heat-hardened
composition, the composition comprising: 65 to 98 weight percent
fumed silica; 1 to 15 weight percent reinforcing filaments; up to
10 weight percent pyrogenic silica; and up to 20 weight percent
opacifier.
2. A base for an electric heater as claimed in claim 1, wherein
the reinforcing filaments are selected from glass, silica, ceramic
fibres, mineral fibres and body soluble fibres.
3. A base for an electric heater as claimed in claim 2, wherein
the glass is selected from E glass, R glass, or S glass, and modifications
thereof.
4. A base for an electric heater as claimed in claim 1, wherein
the opacifier, when provided, is selected from titanium dioxide,
silicon carbide and iron oxide.
5. A base for an electric heater as claimed in claim 4, wherein
the titanium dioxide comprises rutile.
6. A base for an electric heater as claimed in claim 4, wherein
the iron oxide comprises haematite.
7. A base for an electric heater as claimed in claim 1, provided
of dish-like form, having an upstanding wall.
8. A base for an electric heater as claimed in claim 1, additionally
provided with at least one electric heating element secured thereto.
9. A base for an electric heater as claimed in claim 8, wherein
the at least one electric heating element has been secured thereto
during formation of the base by compression of the composition.
10. A base for an electric heater as claimed in claim 8, wherein
a terminal block is secured thereto and electrically connected to
the at least one electric heating element.
11. A base for an electric heater as claimed in claim 8, wherein
the terminal block has been secured thereto during formation of
the base by compression of the composition.
12. A base for an electric heater as claimed in claim 8, wherein
a layer of microporous thermal insulation material of lower thermal
conductivity than the base is provided between the base and the
at least one electric heating element.
13. A method of manufacturing a base for an electric heater comprising
the steps of: 1) providing a composition comprising: 65 to 98 weight
percent fumed silica; 1 to 15 weight percent reinforcing filaments;
up to 10 weight percent pyrogenic silica; up to 20 weight percent
opacifier; 2) compressing the composition to form the base; and
3) heating the base to effect hardening thereof.
14. A method according to claim 13, wherein the heating of the
base to effect hardening thereof is carried out at a temperature
of from 500 to 900 degrees Celsius.
15. A method according to claim 13, wherein the heating of the
base to effect hardening thereof is carried out for a period of
between 15 and 25 minutes.
16. A method according to claim 13, wherein the reinforcing filaments
are selected from glass, silica, ceramic fibres, mineral fibres
and body soluble fibres.
17. A method according to claim 16, wherein the glass is selected
from E glass, R glass, S glass, and modifications thereof.
18. A method according to claim 13, wherein the opacifier, when
provided, is selected from titanium dioxide, silicon carbide and
iron oxide.
19. A method according to claim 18, wherein the titanium dioxide
comprises rutile.
20. A method according to claim 118, wherein the iron oxide comprises
haematite.
21. A method according to claim 13, wherein the base is provided
of dish-like form having an upstanding wall.
22. A method according to claim 13, wherein at least one electric
heating element is additionally provided and secured to the base.
23. A method according to claim 22, wherein the at least one electric
heating element is secured to the base during formation thereof
by compression of the composition.
24. A method according to claim 22, wherein a terminal block is
secured to the base and electrically connected to the at least one
electric heating element.
25. A method according to claim 24, wherein the terminal block
is secured to the base during formation thereof by compression of
the composition.
26. A method according to claim 22, wherein a layer of microporous
thermal insulation material of lower thermal conductivity than the
base is provided between the base and the at least one electric
heating element.
Description [0001] The present invention relates to a base for an electric
heater and a method of manufacture thereof. The invention is particularly,
but not exclusively, concerned with a base for an electric heater
for use in a cooking appliance, such as in a cooking hob with a
glass-ceramic cooking surface, or in an oven.
BACKGROUND TO THE INVENTION
[0002] Electric heaters for cooking appliances are well-known having
a base comprising a metal dish-like support containing a layer of
thermal insulation material, such as microporous thermal insulation
material. An electric heating element is supported on the layer
of insulation material. A wall of thermal insulation material is
also usually provided around the periphery of the heater inside
the metal dish-like support.
[0003] In order to reduce costs, it would be desirable to replace
the metal dish-like support, the layer of thermal insulation material
and the wall of thermal insulation material by a single component
comprising a dish-like base of thermal insulation material in which
the heating element is directly supported. There are two main requirements
for such an arrangement. The dish-like base of thermal insulation
material must have adequate flexural strength so as to be self-supporting
and also low thermal conductivity so as to prevent the outside of
the base reaching an unacceptably high temperature during operation
of a resulting heater.
DESCRIPTION OF PRIOR ART
[0004] Attempts have been made to solve the problem by providing
a base comprising vermiculite and a binder, or comprising mixtures
of vermiculite or mica, pyrogenic silica and optionally reinforcing
fibres, a binder and an opacifier. Such compositions can provide
bases with excellent flexural strength. However, their thermal conductivity
is higher than is desirable and it has been found necessary to provide
a layer of more efficient compacted microporous thermal insulation
material inside the bases and supporting the heating element.
OBJECT OF THE INVENTION
[0005] It is an object of the present invention to overcome or
minimise this problem.
SUMMARY OF THE INVENTION
[0006] According to one aspect of the present invention there is
provided a base for an electric heater comprising a compressed and
heat-hardened composition, wherein the composition comprises:
[0007] 65 to 98 weight percent fumed silica;
[0008] 1 to 15 weight percent reinforcing filaments;
[0009] up to 10 weight percent pyrogenic silica; and
[0010] up to 20 weight percent opacifier.
[0011] According to a further aspect of the present invention there
is provided a method of manufacturing a base for an electric heater
comprising the steps of:
[0012] 1) providing a composition comprising:
[0013] 65 to 98 weight percent fumed silica;
[0014] 1 to 15 weight percent reinforcing filaments;
[0015] up to 10 weight percent pyrogenic silica;
[0016] Up to 20 weight percent opacifier;
[0017] 2) compressing the composition to form the base; and
[0018] 3) heating the base to effect hardening thereof.
[0019] Heat hardening may be at a temperature of from 500 to 900
degrees Celsius.
[0020] Heat hardening may be for a period of between 15 and 25
minutes.
[0021] The reinforcing filaments may be selected from glass, such
as E glass, R glass or S glass, or modifications thereof, silica,
ceramic fibres, mineral fibres and body soluble fibres.
[0022] The opacifier, when provided, may be selected from infrared
scattering materials such as titanium dioxide, which may be in the
form of rutile, zircon, silicon carbide and iron oxide, which may
be in the form of haematite.
[0023] The base may be provided of dish-like form, having an upstanding
wall.
[0024] The base may additionally be provided with at least one
electric heating element secured thereto, whereby an electric heater
is formed. A terminal block may be secured to the base and electrically
connected to the at least one electric heating element.
[0025] The at least one electric heating element and/or the terminal
block may be secured to the base during formation of the base by
compression of the composition.
[0026] A layer of microporous thermal insulation material of lower
thermal conductivity than the base may be provided between the base
and the at least one electric heating element.
[0027] As a result of the present invention, a base for an electric
heater is provided which has adequate flexural strength and low
thermal conductivity. It is not essential to provide additional
thermal insulation of lower thermal conductivity than the base,
although such can be included if desired.
[0028] For a better understanding of the invention and to show
more clearly how it may be carried into effect, the following examples
are given, with reference to the accompanying drawings in which:
BRIEF DESCRIPTION OF THE DRAWINGS
[0029] FIG. 1 is a plan view of an embodiment of a base for an
electric heater according to the present invention;
[0030] FIG. 2 is a cross-sectional view of the base of FIG. 1;
[0031] FIG. 3 is a plan view of an electric heater provided with
the base of FIG. 1;
[0032] FIG. 4 is a cross-sectional view of the heater of FIG. 3;
and
[0033] FIG. 5 is a cross-sectional view of a modified heater having
additional thermal insulation material provided between the base
and the heating element.
EXAMPLES AND PREFERRED EMBODIMENTS
Example 1
[0034] A composition was prepared comprising:
[0035] 98 percent by weight fumed silica, supplied by VAW of Germany;
and
[0036] 2 percent by weight Advantex glass filaments, supplied by
OCF of the USA.
[0037] The composition was compressed in a forming press to form
a base for a heater as denoted by reference numeral 2 in FIGS. 1
and 2. The base 2 had a block density of 700 kilograms per cubic
meter.
[0038] The base 2 was heated at 800 degrees Celsius for 20 minutes
to effect hardening thereof.
[0039] Thermal conductivity was measured for the base 2 and had
a value of 0.105 Watts per meter Kelvin.
[0040] Flexural strength was measured for the base 2 and had a
value of 1400 kilonewtons per square meter.
[0041] During the process of compressing the composition to form
the base 2 for the heater, grooves 4 were also formed in a surface
of the base.
[0042] After the heat-hardening treatment of the base 2, a heating
element 6 of well-known form was secured in the grooves 4, as shown
in FIGS. 3 and 4, and connected to a terminal block 8, to form an
electric heater. Such heater is particular applicable for use in
cooking appliances. The heating element 6 and the terminal block
8 were suitably secured in place by means of a high-temperature-withstanding
adhesive. The terminal block 8 was suitably secured in a recess
10 provided in the base 2 during formation of the base 2.
[0043] A temperature limiter 12 of well-known form can be provided,
traversing the heater and overlying the heating element 6. Such
temperature limiter 12 can have a mounting bracket 14 which is secured
to the outside of the base 2 by means of a suitable adhesive composition.
[0044] Although the base 2 has adequately low thermal conductivity
for most applications, if desired a layer of compacted microporous
thermal insulation material of lower thermal conductivity may be
provided between the base 2 and the heating element 6. Such an arrangement
is illustrated in FIG. 5, in which a layer 16 of the compacted microporous
thermal insulation material is provided between the base 2 and the
heating element 6.
Example 2
[0045] A composition was prepared comprising:
[0046] 96 percent by weight fumed silica, supplied by VAW of Germany;
[0047] 2 percent by weight Advantex glass filaments, supplied by
OCF of the USA; and
[0048] 2 percent by weight pyrogenic silica type A200, supplied
by Degussa-Huls of Belgium.
[0049] This composition, together with a heating element attached
to its terminal block, was placed in a mould and compressed to form
a heater unit. The compressed composition had a block density of
600 kilograms per cubic meter. The complete unit was heated at 800
degrees Celsius for 20 minutes.
[0050] The resulting heater was as shown in FIGS. 3 and 4, comprising
a base 2 of the heat-hardened composition, together with a heating
element 6 and terminal block 8.
[0051] The heating element 6 and terminal block 8 were moulded
into the base 2 and required no additional securing means.
[0052] The base 2 had a thermal conductivity of 0.0661 Watts per
meter Kelvin and a flexural strength of 1135 kilonewtons per square
meter.
Example 3
[0053] A composition was prepared comprising:
[0054] 93 percent by weight fumed silica, supplied by VAW of Germany;
[0055] 2 percent by weight Advantex glass filaments, supplied by
OCF of the USA; and
[0056] 5 percent by weight pyrogenic silica type A200, supplied
by Degussa-Huls of Belgium.
[0057] This composition, together with a heating element attached
to its terminal block, was placed in a mould and compressed to form
a heater unit. The compressed composition had a block density of
500 kilograms per cubic meter. The complete unit was heated at 800
degrees Celsius for 20 minutes.
[0058] The resulting heater was as shown in FIGS. 3 and 4, comprising
a base 2 of the heat-hardened composition, together with a heating
element 6 and terminal block 8.
[0059] The base 2 had a thermal conductivity of 0.0608 Watts per
meter Kelvin and a flexural strength of 730 kilonewtons per square
meter.
Example 4
[0060] A composition was prepared comprising:
[0061] 93 percent by weight fumed silica, supplied by VAW of Germany;
[0062] 2 percent by weight Advantex glass filaments, supplied by
OCF of the USA; and
[0063] 5 percent by weight silica type R974, supplied by Degussa-Huls
of Germany.
[0064] This composition, together with a heating element attached
to its terminal block, was processed in exactly the same way as
that of Example 3, to form a heater as shown in FIGS. 3 and 4, comprising
a base 2 of the heat-hardened composition, together with a heating
element 6 and terminal block 8.
[0065] The base 2 had a thermal conductivity of 0.0611 Watts per
meter Kelvin and a flexural strength of 770 kilonewtons per square
meter.
Example 5
[0066] A composition was prepared comprising:
[0067] 83 percent by weight fumed silica, supplied by VAW of Germany;
[0068] 10 percent by weight rutile opacifier, supplied by Tilcon,
UK;
[0069] 2 percent by weight Advantex glass filaments, supplied by
OCF of the USA; and
[0070] 5 percent by weight pyrogenic silica type R200, supplied
by Degussa-Huls of Germany.
[0071] This composition, together with a heating element attached
to its terminal block, was placed in a mould and compressed to form
a heater unit. The compressed composition had a block density of
600 kilograms per cubic meter. The complete unit was heated at 800
degrees Celsius for 20 minutes.
[0072] The resulting heater was as shown in FIGS. 3 and 4, comprising
a base 2 of the heat-hardened composition, together with a heating
element 6 and terminal block 8.
[0073] The base 2 had a thermal conductivity of 0.054 Watts per
meter Kelvin and a flexural strength of 670 kilonewtons per square
meter.
[0074] The foregoing examples demonstrate that a base for an electric
heater having a composition based on fumed silica can be provided
having adequate flexural strength and low thermal conductivity.
Improved thermal conductivity and improved flow characteristics
during compression are achieved by including a small amount of pyrogenic
silica in the composition, while still retaining adequate flexural
strength.
COMPARATIVE EXAMPLES
Comparative Example 1
[0075] A composition was prepared comprising:
[0076] 60 percent by weight pyrogenic silica type A200, supplied
by Degussa-Huls of Germany;
[0077] 37 percent by weight rutile opacifier, supplied by Tilcon,
UK; and
[0078] 3 percent by weight Advantex glass filaments, supplied by
OCF.
[0079] The composition was compressed to form a base 2 for an electric
heater, as shown in FIGS. 1 and 2. The block density was 350 kilograms
per cubic meter.
[0080] The resulting base 2 exhibited very low thermal conductivity
of 0.0301 Watts per meter Kelvin. However its flexural strength
of 110 kilonewtons per square meter was insufficiently high for
the base to be used for an electric heater.
Comparative Example 2
[0081] A composition was prepared comprising:
[0082] 80 percent by weight Microfine Vermiculite, supplied by
Hoben Davis, UK; and
[0083] 20 percent by weight type K66 binder, supplied by Crosfield,
UK.
[0084] The composition was compressed to form a base 2 for an electric
heater, as shown in FIGS. 1 and 2. The block density was 700 kilograms
per cubic meter. The resulting base 2 was heat treated at 300 degrees
Celsius for 20 minutes.
[0085] Although the base had excellent flexural strength of 1960
kilonewtons per square meter, its thermal conductivity was unacceptably
high, having a value of 0.36 Watts per meter Kelvin.
Comparative Example 3
[0086] A composition was prepared comprising:
[0087] 62 percent by weight Microfine Vermiculite, supplied by
Hoben Davis, UK;
[0088] 20 percent by weight type K66 binder, supplied by Crosfield,
UK; and
[0089] 18 percent by weight pyrogenic silica, type A200, supplied
by Degussa-Huls of Belgium.
[0090] The composition was compressed to form a base 2 for an electric
heater, as shown in FIGS. 1 and 2. The block density was 700 kilograms
per cubic meter. The resulting base was heat treated at 300 degrees
Celsius for 20 minutes.
[0091] Although the base had excellent flexural strength of 1813
kilonewtons per square meter, its thermal conductivity was unacceptably
high, having a value of 0.25 Watts per meter Kelvin. |